Double-crosslinked self-degradable hydrogel for temporary plugging in low temperature reservoirs 认领 引用
1
作者 Tai-Heng Yin Yu-Meng Zhu +6 位作者 Yu-Qi Yang Shen-Gen Chen Ji-Rui Chen Yuan-Yuan Lu Han-Yu Guo Tao Wan Jian Liu 《Petroleum Science》 SCIE EI CAS CSCD 2026年第3期1402-1415,共14页
Temporary plugging agents are critical to oilfield operations such as diversion fracturing,wellbore interventions,and drilling.This study develops a double-crosslinked self-degradable gel(DSDG)using polydopamine and p... Temporary plugging agents are critical to oilfield operations such as diversion fracturing,wellbore interventions,and drilling.This study develops a double-crosslinked self-degradable gel(DSDG)using polydopamine and poly(ethylene glycol)diacrylate as crosslinkers for polyacrylamide,targeting low temperature reservoirs.The DSDG system integrates covalent crosslinking via C=C bonds and dynamic crosslinking through amine–catechol interactions.Gelation kinetics,rheological properties,self-degradation mechanisms,and gel breaking performance of DSDG were systematically characterized.By analyzing the influence of components on gelation kinetics and mechanical properties,the composition of DSDG was optimized to include 4–8 wt%acrylamide monomer,0.5–0.8 wt%initiator,and 0.2–0.6 wt%poly(ethylene glycol)diacrylate crosslinker,with a dopamine to acrylamide mass ratio of(5–8)×10−3.At 60–80℃,DSDG transitions from liquid to quasi-solid gel within 30–180 min,with>80%of the gelation process occurring in a low viscosity phase conducive to pumpable injection.Unoxidized catechol groups,π–πstacking,and hydrogen bonding synergistically enhance tensile strength,fracture toughness,and interfacial adhesion,enabling robust sealing under downhole stresses.Core flooding tests in 5–50 mD cores achieved initiation and breakthrough pressure gradients of 34.6–119 and 86.6–184.6 MPa/m,respectively.In simulated wellbore with an inner diameter of 120 mm,the pressure-bearing capacity reached 1.25 MPa/m.Acidic/alkaline conditions rapidly degrade polydopamine,disrupting network integrity and enabling controllable gel breaking times of 1–20 d.Free dopamine monomers inhibit acrylamide polymerization,reducing post-degradation viscosity to<10 mPa·s via shortened polyacrylamide chains. 展开更多
关键词 Self-degradable Double-crosslinked hydrogel Polydopamine Low temperature reservoir Temporary plugging agent